PA66-GF30 Polyamide 66 30%GF reinforced PA66 resin price PA66 PA6 price raw material

pa66-gf30 polyamide66 30%gf reinforced pa66 resin price pa66 PA6 price raw materialGlass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.It is high strength, high toughness, wear resistance and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperat

Featured Products

pa66-gf30 polyamide66 30%gf reinforced pa66 resin price pa66 PA6 price raw material
PA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw Material
Glass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.

It is high strength, high toughness, wear resistance and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good electrical insulation, good surface smoothness, easy molding and other advantages.

Material is approved by RoHS compliant, and can be widely used in automotive parts, electronic appliances, power tools, gears, mechanical parts and other fields.
PA66 (F0750)
 Product Description Applications
·50%66  50% glass fiber reinforced PA66· Injection molding
·  Excellent heat stability· Good mechanical properties balance
 Properties Test Method Test Condition UnitTypical Values
Physical properties
Specific Gravity ISO 118323ºC g/cm31.58
Ash ISO 3451800ºC,30min 50
Mechanical properties
Tensile Strength ISO 527 50mm/min MPa 230
Elongation at BreakISO 527 50mm/min %2
Flexural Modulus ISO 1782mm/min MPa 14500
Charpy Notched Impact Strength     ISO 179-1eA23ºCkJ/m2 17
Charpy Unotched Impact Strength     ISO 179-1eU23ºCkJ/m2 85
Thermal properties
Heat deflection temperatureISO 751.80MPaC250
Melting PointDSC-C262
Other properties
Flammability TL1010-mm/min SE
Note: The data above is typical value for reference, not guarantee value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the material, please consult with TOPO.
 Processing Conditions Range 
Melt Temperature260-280ºC
Mold Temperature50-80ºC
Pre-Dry needed110ºC, 4-8h
Note: The above process condition is only for reference. The actual process should be adjusted according to different type of machine,  mold design and product design.

PA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw Material
PA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw MaterialPA66-GF30 Polyamide66 30%GF Reinforced PA66 Resin Price PA66 PA6 Price Raw Material

Are you trading company or manufacturer?

We are manufacturer.

 

About Sample?

5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.


How does your factory control the quality?
Quality is the Priority, we always pay great important to quality from beginning to  end, we have  professional QC  for item quality from spare parts to finished goods.

 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? is the sample free? 

7-10 days to send free samples by DHL, TNT, UPS

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours